Pengaruh Variasi Holding Time Pada Proses Heat Treatment (Hardening) Untuk Baja S50c Sebagai Pisau Mesin Pencacah Kayu

  • Muhammad Hisson Alfariji Munandar Program studi teknik mesin, Universitas Singaperbangsa Karawang
  • Kardiman Kardiman Universitas Singaperbangsa Karawang
  • Deri Teguh Santoso Universitas Singaperbangsa Karawang
https://doi.org/10.29407/jmn.v6i2.20304
Abstract views: 238 , PDF downloads: 45
Keywords: S50C Steel, Hardening, Holding time, Hardness, Microstructure

Abstract

S50C Alloy Steel is a widely produced and used medium carbon alloy steel, which serves as a raw material for manufacturing machine components, building structures, tools, and one of them being knife blades for wood chippers. The aim of this research is to determine the hardness value and microstructural changes in S50C steel after the heat treatment of hardening and holding time. The method used in this study is an experimental method, where S50C steel is subjected to heat treatment at a temperature of 850°C, followed by different holding times of 30, 60, and 90 minutes, and then cooled using oil. The research results show that the highest hardness value in S50C steel, treated with rapid cooling using oil, has an average hardness value of 589.29 HV after a 90-minute holding time, compared to the raw material's hardness of 262.67 HV. Microstructural testing reveals that the microstructure of the raw material consists of ferrite and pearlite with balanced crystal shape and size, in accordance with a carbon content of 0.50%. In the group of specimens undergoing rapid cooling with oil in the hardening process, a new microstructure called martensite is obtained, which is the main structure responsible for the increased hardness of the steel.

Downloads

Download data is not yet available.

References

I. Gata, B. Suharno, B. Harjanto, dan M. Eng, “PENGARUH VARIASI TEMPERATUR DAN HOLDING TIME DENGAN MEDIA QUENCHING OLI MESRAN SAE 40 TERHADAP STRUKTUR MIKRO DAN KEKERASAN BAJA ASSAB 760.”

IRAWATI ADELINA, “ANALISA PENGARUH VARIASI WAKTU PENAHANAN AUSTENISASI PADA PERLAKUAN PANAS PENGERASAN TERHADAP STRUKTUR MIKRO, NILAI KEKERASAN DAN KEKUATAN IMPAK PADA BAJA KARBON AISI 1050,” Tugas Akhir, Institut Teknologi Sepuluh Nopember Surabaya , Surabaya, 2017.

A. Ibrahim, Jufriad, dan M. Nur Mujaddedy, “ANALISA PENGARUH QHUENCHING DAN TEMPERING TERHADAP SIFAT MEKANIK PADA BAJA AISI 1050,” Mesin Sains Terapan, vol. 4, 2020.

J. Hasil Karya Ilmiah, D. Joko Purnomo, S. Jokosisworo, dan U. Budiarto, “JURNAL TEKNIK PERKAPALAN Analisa Pengaruh Holding Time Tempering Terhadap Kekerasan, Keuletan, Ketangguhan dan Struktur Mikro Pada Baja ST 70,” Jurnal Teknik Perkapalan, vol. 07, no. 1, 2019, [Daring]. Tersedia pada: https://ejournal3.undip.ac.id/index.php/naval

Sidney, H, dan Anver, Introduction to Physical Metallurgy, 2nd ed. Singapore: McGraw-Hill, Inc., 1974.

P. Trihutomo, A. Kekerasan, P. Berbahan, dan B. Karbon, “ANALISA KEKERASAN PADA PISAU BERBAHAN BAJA KARBON MENENGAH HASIL PROSES HARDENING DENGAN MEDIA PENDINGIN YANG BERBEDA.”

W. A. Arzak, “ANALISIS SIFAT MEKANIS PADA MATA PISAU MESIN SERUT KAYU BERBAHAN BAJA KARBON SEDANG HASIL PROSES HARDENING DENGAN VARIASI MEDIA PENDINGIN.”

S. Sudianto, “Perbandingan Pemahaman Matematika Siswa antara yang Menggunakan Adobe Flash CS3 dengan Software iMindMapTM pada Pokok Bahasan Limit Fungsi,” vol. 1, 2019.

Dieter, Metalurgi Mekanik. Jakarta: Erlangga, 1985.

R. Dwisaputro, M. Saiful Anwar, dan Rusnaldy, “PENGARUH PERLAKUAN PANAS BAJA TAHAN KARAT MARTENSITIK AISI 410 TERHADAP STRUKTURMIKRO DAN KETAHANAN KOROSI,” Metalurgi, vol. 5, 2018.

G. Suhandoyo, “ANALISA PENGARUH MEDIA PENDINGINAN NANOFLUIDA PARTIKEL Al2O3 PADA PROSES QUENCHING – TEMPERING TERHADAP SIFAT MEKANIS DAN STRUKTUR MIKRO BAJA AISI 4140,” 2022.

PlumX Metrics

Published
2023-12-31
How to Cite
[1]
M. H. Alfariji Munandar, K. Kardiman, and D. T. Santoso, “Pengaruh Variasi Holding Time Pada Proses Heat Treatment (Hardening) Untuk Baja S50c Sebagai Pisau Mesin Pencacah Kayu”, JMN, vol. 6, no. 2, pp. 127-136, Dec. 2023.
Issue
Vol. 6 No. 2 (2023): Jurnal Mesin Nusantara
Section
Articles

Authors who publish with this journal agree to the following terms:

  1. Copyright on any article is retained by the author(s).
  2. The author grants the journal, right of first publication with the work simultaneously licensed under a Creative Commons Attribution License that allows others to share the work with an acknowledgment of the work’s authorship and initial publication in this journal.
  3. Authors are able to enter into separate, additional contractual arrangements for the non-exclusive distribution of the journal’s published version of the work (e.g., post it to an institutional repository or publish it in a book), with an acknowledgment of its initial publication in this journal.
  4. Authors are permitted and encouraged to post their work online (e.g., in institutional repositories or on their website) prior to and during the submission process, as it can lead to productive exchanges, as well as earlier and greater citation of published work.
  5. The article and any associated published material is distributed under the Creative Commons Attribution-ShareAlike 4.0 International License